Anisotropic icephobic and biocidal coatings

ABSTRACT

Articles including durable and icephobic and/or biocidal polymeric coatings are disclosed. The polymeric coatings can include a bonding layer which may contain a substantially fully cured polymeric resin providing excellent adhesion to metallic or polymer substrates. The polymeric coating further includes an outer surface layer which is smooth, hydrophobic, biocidal and icephobic and, in addition to a substantially fully cured resin, contains silicone comprising additives near the exposed outer surface. The anisotropic polymeric coatings are particularly suited for strong and lightweight parts required in aerospace, automotive and sporting goods to applications. A process for making the articles is disclosed as well.

CROSS REFERENCE TO RELATED APPLICATIONS

The present invention is a continuation of U.S. application Ser. No. 16,924,301 filed Jul. 9, 2020, which is a continuation-in-part of U.S. application Ser. No. 16/515,093, filed Jul. 18, 2019, the entirety of each application is incorporated herein by reference.

FIELD OF THE INVENTION

The invention relates generally to an article of manufacture comprising a durable exposed surface which is hydrophobic, has low ice adhesion and/or provides biocidal properties. The inventive coating is applied to at least part of an outer surface of the article. The inventive coating comprises a layered or graded structure containing (i) a bonding layer in intimate contact with a metallic, polymeric or composite substrate and (ii) an outer, exposed icephobic layer containing a silicone additive and optionally a biocidal additive. The anisotropic and durable water-repellent coating may contain distinct sublayers and/or a gradual transition from one chemical composition to another. The invention further relates to a process for fabricating the article.

BACKGROUND OF THE INVENTION

Self-cleaning, superhydrophobic, biocidal and icephobic coatings are of great interest for use in transportation, consumer, sporting goods and other commercial applications where an article is exposed to environmental elements and/or comprises touch surfaces. Ice accumulation on power lines as well as a variety of vehicles, such as surface or marine vehicles as well as airplanes, can poses significant challenges. The buildup of ice on aerospace components such as wings, propellers and jet engine parts is a significant safety concern and a variety of approaches have been attempted to provide means of preventing ice accumulation. Other concerns include spreading of infectious diseases via touch-surfaces in homes, offices, and public institutions.

Various patent filings address the modification of outer surfaces of articles to increase water repellency:

Victor et. al. in U.S. Pat. No. 8,486,319 (2013), assigned to the same assignee as the present application, disclose super-hydrophobic and self-cleaning articles with a polymeric outer roughened/textured surface created by imprinting exposed surfaces with suitable fine-grained and/or amorphous metallic embossing dies to transfer a dual surface structure, including ultra-fine features less than or equal to 100 nm embedded in and overlaying a surface topography with macro-surface structures greater than or equal to 1 μm.

Similarly, various patent filings address coatings applied to outer exposed surfaces of articles, e.g., to render them icephobic:

Putnam et. al. in US 2006/0281861 disclose liquid and/or solid anti-icing fillers and/or oils which are combined with erosion resistant silicone and/or fluorocarbon elastomeric materials to form erosion-resistant and icephobic coatings. These coatings may be utilized to prevent ice build-up on various gas turbine engine components, aircraft components, watercrafts, power lines, and telecommunication lines. Putnam provides no information on adhesion strength between the icephobic coating and the underlying substrate.

Hoover et. al. in U.S. Patent Publication 2007/0254170 disclose a process for protecting an article such as a gas turbine engine fan blade using an anti-icing coating comprising at least one “polysiloxane free of additives” and curing the anti-icing composition to form an anti-icing coating exhibiting an ice shear strength of about 19 kPA to about 50 kPa. The anti-icing coating composition described was identified as the commercially available NuSil™ R-2180 product from NuSil Technology, LLC, Santa Barbara, Calif., USA which is a two-part silicone elastomer dispersed in xylene. Hoover provides no information on adhesion strength between the icephobic coating and the underlying substrate.

Byrd et. al. in U.S. Pat. No. 7,202,321 (2007) disclose a method for applying a polysiloxane-containing coating to a substrate, said coating preferably comprising a polysiloxane(amide-ureide). The coating is durable, long lasting, corrosion-resistant and icephobic. Byrd provides no information on adhesion strength between the icephobic coating and the underlying substrate.

Butts et. al. in U.S. Patent Publication 2011/0143148 disclose an article comprising a weather resistant coating on its outer surface exposed to precipitation or airborne debris. The coating comprises two components: (a) a one-part or two-part room temperature vulcanizable polyorganosiloxane composition; and (b) an ice release-enhancing proportion of at least one polyorganosiloxane composition comprising one or more silanol or alkoxy-silyl groups and comprising from about 10 weight percent to about 85 weight percent of at least one hydroxy-terminated or alkoxy-terminated polyoxyalkylenealkyl radical. In another embodiment, an article comprises a weatherable surface exposed to precipitation or airborne debris; and a weather resistant coating disposed on the weatherable surface, wherein the coating includes a one-part or two-part addition curable polyorganosiloxane composition comprising a resin polymer and a crosslinker, wherein the resin polymer and/or crosslinker comprises an ice release-enhancing proportion of covalently bound hydrophilic functionality that contains between about 0.5 weight percent to about 40 weight percent of the coating composition. Butts provides no information on adhesion strength between the icephobic coating and the underlying substrate.

Nowak et. al. in U.S. Patent Publication 2014/0162022 disclose structural coatings with dewetting and anti-icing properties which are impact-resistant, and coating precursors for fabricating same. Dewetting and anti-icing performance is simultaneously achieved in a structural coating comprising multiple layers, wherein each layer includes (a) a continuous matrix; (b) discrete templates dispersed that promote surface roughness to inhibit wetting of water; and (c) nanoparticles that inhibit heterogeneous nucleation of water. These structural coatings can be applied by spraying and the use of multiple layers extends the lifetime, as in case the surface is damaged during use, freshly exposed surface will expose a coating identical to that which was lost. Nowak provides no information on adhesion strength between the icephobic coating and the underlying substrate.

Harmer et. al. in WO 2015/094917 disclose substrates coated with a multilayer film having low ice adhesion. The multilayer film comprises a first layer that is a polymer having a thickness of greater than 0.9 mm and less than 10 mm, a Shore A hardness of less than about 100 and a flex modulus in the range of from 1 kPa to 100 GPa. The second film layer of the multilayer film is a polymer that has a thickness of less than 100 μm, a water contact angle of greater than 60°. The first second film layers can flex without separating or without forming cracks. Harmer provides no information on adhesion strength between the icephobic coating and the underlying substrate.

Tuteja et. al. in WO 2016/176350 disclose durable icephobic coatings for aircrafts, powerlines, vehicles, marine structures, communications towers, outdoor equipment, and the like. The icephobic material may comprise an elastomeric polymer with a low crosslink density (e.g., ≤1,300 mol/m³) and low initial ice adhesion strength (e.g., τ_(ice)≤100 kPa prior to exposure to icing conditions). Furthermore, the icephobic material maintains τ_(ice) after 10 icing/deicing cycles that is >50% of the initial τ_(ice). Introducing optional miscible liquids enhances interfacial slippage of chains in the elastomeric polymer. The low τ_(ice) levels minimize ice buildup and any accumulated ice spalls off during normal operation. Other icephobic materials include linear polymers with plasticizers distributed therein or PDMS-silane coatings, both of which are free of any layers of surface liquids. Tuteja provides no information on adhesion strength between the icephobic coating and the underlying substrate.

Similarly, various patent filings address coatings applied to outer exposed surfaces of articles to render them biocidal:

Masters et. al. in U.S. Pat. No. 7,934,888 (2011) disclose marine anti-fouling coatings comprising a metal, metal alloy or compounds of one or more metallic elements and can include any one or more metals from groups Ib, IIa, IIb, IIIa, IIIb, IVa, IVb, Va, Vb, VIb, VIIb, and VIII of the Periodic Table of Elements. Masters provides no information on adhesion strength between the antimicrobial coating and the underlying substrate.

Krasnow et. al. in U.S. Pat. No. 10,034,478B2 (2018) disclose various compositions having antimicrobial activity containing surface functionalized particles comprising an inorganic copper salt which has low water solubility. Krasnow provides no information on adhesion strength between the antimicrobial coating and the underlying substrate.

Palumbo et. al. in WO 2018/112603, assigned to the same assignee as the present application, disclose anti-bacterial leg bands for the prevention of foot rot, interdigital dermatitis and other bacterial infections in livestock. Durable articles applied to the body of animals comprise grain-refined and/or amorphous metals, e.g., copper, cobalt, tin and zinc, or their combinations, in contact with a fluid absorbent material. According to Palumbo the antimicrobial efficacy can be improved via grain size reduction and is also known to increase the hardness, strength, abrasive wear, cuff- and scratch resistance. In one embodiment grain-refined and/or amorphous metallic layers comprise metal flakes, powders and the like, processed into coherent “metallic bands” by using, e.g., an organic binder.

Facchini et. al. in U.S. Pat. No. 8,691,397 (2014), assigned to the same assignee as the present application, disclose various biocidal metallic layers comprising cobalt. Free standing articles or articles at least partially coated with substantially porosity free, fine-grained and/or amorphous Co-bearing metallic materials optionally containing solid particulates dispersed therein, are disclosed. The electrodeposited metallic layers and/or patches comprising Co provide, enhance or restore strength, wear and/or lubricity of substrates in applications requiring anti-microbial properties.

Burrell et al. in U.S. Pat. No. 5,753,251 (1998), U.S. Pat. No. 5,681,575 (1997), U.S. Pat. No. 5,837,275 (1998), U.S. Pat. No. 6,238,686 (2001) and U.S. Pat. No. 6,365,220 (2002) teach the synthesis of antimicrobial metals that exhibit enhanced antimicrobial activity that is intrinsic to the bulk metal by virtue of its high stored internal energy. The sustained ionic dissolution rate is due to the ultrafine-grained microstructure of the metallic films. The enhanced, sustained anti-microbial effect is associated with the processing of metals and alloys in fine-grained form, however, the material processing technique of Burrell et al. is based upon vapor deposition methods such as physical vapor deposition (PVD) and chemical vapor deposition (CVD). While such techniques are suitable for the synthesis of fine-grained anti-microbial materials, they are unsuitable for the production of highly abrasive wear, scratch and scuff-resistant surfaces as the resulting vapor deposited coatings are generally thin (typically micron thickness), porous (<99% theoretical density) and are oftentimes relatively soft (<200 VHN).

Thus, there is a particular need for articles containing an adherent, durable, hydrophobic, icephobic and/or biocidal polymeric coating on their outer surface.

SUMMARY OF THE INVENTION

A variety of articles are made of metallic materials that are used in atmospheric conditions where their outer surface is exposed to rain, snow and/or ice and/or constitute touch-surfaces which may transmit diseases. It is also well known that relatively thin, grain-refined and/or amorphous metallic coating can be applied to softer metals, including, but not limited to, Al and Ti, as well as polymeric materials, including, but not limited to, thermoplastics and thermosets which may be filled with, e.g., carbon or glass fibers for use in applications requiring high specific strength and durability. It is also well known that articles made from conventional, unfilled/unreinforced as well as fiber reinforced polymers (FRP) and carbon fiber reinforced polymers (CFRP) are frequently employed in outdoor applications including, but not limited to, sporting goods as well as in transportation systems such vehicles traveling on land, in water or air.

As noted above, it is known to minimize the adverse effect of atmospheric conditions on articles made of various metals as well as articles comprising non-metallic substrates, e.g., polymer and polymer composite substrates, by applying a coating on their outer surface to render them water repellent and/or to lower ice adhesion. For instance, per-fluoroalkyl silanes have been employed in surface coatings to reduce ice adhesion. However, compositions of this type lose their water-repellency rather quickly and need to be regenerated frequently, i.e., they are considered to contain “consumable” components. Quaternary ammonium siloxane-based materials have been incorporated, e.g., into windshield washing fluids, but this approach fails to provide a durable anti-icing coating and readily washes away during use. Attempts to utilize silicone rubbers, silicone oils and polyisoprenes have not been successful as they undergo rapid wear, are lost from the outer surface and furthermore they take up oils and dirt. Furthermore, typical additives used to lower ice adhesion including, but not limited to, silicones, also reduce the adhesion of the coating to its underlying substrate causing the coating to delaminate and spall off during use.

The inventors of the present disclosure have recognized that selected properties desired of the icephobic coating on the exposed outer surface are diametrically opposed to selected properties required on the inner surface of the icephobic coating which is in intimate contact with the underlying article/substrate. The inventors have surprisingly discovered that a multilayered or graded organic coating applied to the metallic or polymeric substrates provides unprecedented hydrophobicity, icephobicity, durability and adhesion while providing excellent cohesive strength. The inventors have furthermore discovered that icephobic coatings can be designed to be hydrophilic or hydrophobic although, in general, hydrophobic surfaces are preferred as such coatings repel water as well as readily shed snow and ice.

The inventors of the present disclosure have also discovered that the outer surface of the inventive coating be preferably smooth (R_(a)<1 μm), as textured/roughened surfaces such as textured superhydrophobic surfaces, under certain conditions, can have increased ice adhesion, particularly in the case of frost formation and only show low ice-adhesion if a liquid, e.g., supercooled water droplets, hit the surface. In contrast, the inner surface of the inventive coating at any solid interface is preferably rough (R_(a)>1 μm) to enhance the adhesion between the coating and, e.g., the underlying substrate.

Recently various infections with serious health implications to the general population have been spreading worldwide. Precautionary measures to prevent infections include hand washing as well as the use of personal protective equipment including, but not limited to, gloves, gowns, various face masks, eye protections and face shields. Similarly, a variety of products ranging from high touch surfaces encountered in homes, offices, public places such as door handles, arms of reception area chairs, elevator buttons, stair railings, common area devices, restroom surfaces medical instruments and equipment must be properly sterilized to ensure they are not contaminated to prevent spreading of diseases. High touch surfaces require frequent cleaning and disinfecting with antimicrobial agents. As an alternative, to better protect the population it is desirable to incorporate fast-acting, highly efficient, antimicrobial properties, including antiviral properties, in outer surfaces in a variety of different applications. The inventors of the present disclosure have also discovered that the polymeric coatings can be rendered biocidal by incorporating powders of metals and metal compounds, including but not limited to Cu, Ag, Co, Ni, Sn and Zn and alloys comprising at least one of the metals listed, into their formulations. Preferred biocidal powder additions are metals or their oxides, however, salts including metal halides and sulfates can be used as well, Preferably, metal or metal alloy powders, having a particle size in the range of 1-500 microns and having a microstructure composed of nanocrystalline grains with an average grain size in the range of 5-500 nm and/or an amorphous microstructure, are used.

The inventors have also surprisingly discovered that the addition of metal powders and/or metal compounds to the polymeric coatings described herein provides benefits to durability, cohesive strength and adhesion while, if properly designed, surprisingly not compromising the icephobic behavior or rendering the coating hydrophilic, In addition, metal and/or carbon additions renders the coating electrically conductive which is desirable in many applications, e.g., for EMI shielding and in applications where damage can occur in the event of lightning strikes.

The present invention describes in-part an antimicrobial material composition that can be applied to various substrates and protective articles.

It is therefore an objective of the present invention to utilize articles made of durable polymeric materials or metallic materials comprising an amorphous and/or crystalline microstructure and rendering the outer surface hydrophobic and/or icephobic and/or biocidal by applying an adherent, polymeric, durable, hydrophobic and/or icephobic and/or biocidal coating.

It is an objective of the present invention to provide articles wherein the inventive material coating surface extends over between 1% and 100% of the total exposed outer surface of the article.

It is an objective of the present invention to provide inventive coatings having a total thickness of at least 10 microns, preferably in the range of 25 to 250 microns (cured loading: ˜3-30 mg/cm²), preferably between 50 and 100 microns (cured loading: ˜6-12 mg/cm²).

It is an objective of the present invention to provide durable, scratch and abrasion resistant, strong, lightweight articles for use in various applications including, but not limited to, transportation applications (including automotive, aerospace, ships and other vessels navigating on land, in air, space and on water, and their components), defense applications, industrial components, building materials, consumer and commercial products, electronic equipment or appliances and their components, sporting goods as well as any other indoor or outdoor equipment.

It is an objective of the present invention to render the outer surface of articles water repellent/hydrophobic with a contact angle for water greater than 90°, preferably greater than 120°, and preferably super-hydrophobic (contact angle for water greater than 150°).

It is an objective of the invention to render the outer surface of articles self-cleaning by suitably creating a low roll-off angle (tilt angle for water less than 25°), preferably a tilt angle for water less than 20°, more preferably less than 10° or even 5°, by an economic, convenient and reproducible process.

It is an objective of the present invention to achieve excellent adhesion between the organic coating and the outer surface of articles by creating a rough/textured surface at the interface between the article/substrate and the applied coating, i.e., generating a surface roughness (R_(a)) of more than 0.5 microns, preferably more than 0.75 microns, and more preferably more than 1 microns.

It is an objective of the present invention to render the outer surface of articles hydrophobic, icephobic and biocidal by applying a coating with a smooth exposed surface characterized by a surface roughness (R_(a)) less than or equal to 2 microns, preferably less or equal to 1 micron, preferably less or equal to 0.75 microns, and more preferably less or equal to 0.5 microns.

It is an objective of the present invention to render the outer surface of an article biocidal by applying a coating containing powder additions of biocidal metals and metal compounds.

It is an objective of the present invention to provide biocidal coatings displaying a “radius of no growth” on the zone inhibition test for salmonella or listeria after 24 hours at 37° C. of greater than 0.1 mm, preferably greater than 0.5 mm and more preferably greater than 1mm and up to 50 mm.

It is another objective of the present invention to provide a coating having a durable polymeric outer layer which at room temperature, in its cured form, does not contain any fluids, e.g., silicone oils.

It is an objective of the present invention to provide lightweight articles comprising, at least in part, liquid repellent and/or self-cleaning outer surfaces which also display low ice-adhesion strength which are biocidal with increased wear, erosion and abrasion resistance, durability, strength, stiffness, thermal conductivity and thermal cycling capability.

It is an objective of the present invention to provide an outer surface with a low ice-adhesion strength which is largely maintained after repeated icing/deicing cycles using, after curing, solid and “permanent” icephobic additions as opposed to, after curing, sacrificial, consumable icephobic additions such as lubricating liquids such as oils which rapidly get consumed and/or lost from the surface resulting in a rapid rise of the ice-adhesion strength with repeated icing/deicing cycles or time exposed to the environmental elements due to, among other, wind, rain, and ice erosion.

It is an objective of the present invention to provide coated articles with an outer surface having an ice-adhesion strength on the first cycle, as well as on the 5^(th) or 7^(th) cycle, of no greater than 700 kPa, preferably no greater than 500 kPa, preferably no greater than 400 kPa, preferably no greater than 350 kPa, preferably no greater than 200 kPa, and more preferably no greater than 150 kPa, when measured according to ERDC/CRREL Technical Note 03-4.

It is an objective of the present invention for the outer surface of the coated articles to have a Shore D-scale hardness of at least 10, preferable 15, preferable 20, preferable 25, preferably 40, more preferably 50, and more preferably 60.

It is an objective of the present invention for the outer surface of the coated articles disclosed to have a sand erosion value according to standard ASTM G76 at 90 degrees of less than 10 mm³/kg, preferably less than 7.5 mm³/kg, and preferably less than 5 mm³/kg.

It is an objective of this invention to provide coated articles composed of icephobic, polymeric outer coatings on metallic material substrates including, but not limited to, Al, Co, Cu, Fe, Ni, Sn, Ti and Zn and their alloys, and/or polymeric material substrates including, but not limited to, polyamides and carbon fiber composites, having a “pull-off strength” between the substrate/article and the icephobic outer layer according to standard ASTM 4541D of at least 250 psi (1.73MPa), preferably at least 300 psi, preferably at least 400 psi, preferably at least 500 psi, preferably at least 750 psi, preferably at least 1,000 psi and preferably at least 1,200 psi.

It is an objective of this invention to provide coated articles composed of a icephobic polymeric outer coatings on metallic and/or polymeric materials showing no failure such as delamination according to ASTM B553-71for service condition 1 (60° C. to −30° C.), preferably service condition 2, preferably service condition 3 and even more preferably for service condition 4.

It is an objective of this invention to provide coated articles capable of withstanding 1, preferably 5, more preferably 10, more preferably 20 and even more preferably 30 temperature cycles without failure according to ANSI/ASTM specification B604-75 section 5.4 (Standard

Recommended Practice for Thermal Cycling Test for Evaluation of Electroplated Plastics ASTM B553-71) for service condition 1 (60° C. to −30° C.), preferably service condition 2, preferably service condition 3 and even more preferably for service condition 4.

It is an objective of the present invention to provide coated articles with at least in part icephobic and liquid repellent and/or self-cleaning and/or biocidal outer surfaces for a variety of applications including, but not limited to:

-   aerospace parts and components including, but not limited to, wings,     wing parts including flaps and access covers, structural spars and     ribs, propellers, rotors and rotor blades, stators and stator vanes,     rudders, covers, fuselage parts, nose cones, and landing gear; -   automotive components including, but not limited to, heat shields,     oil, transmission and brake parts, fluid tanks and exposed housings     including oil and transmission pans, spoilers, grill-guards and     running boards, vehicle chassis parts including hood, doors and side     panels, gas tanks and engine covers; -   sporting goods including, but not limited to, hockey sticks, skate     blades, helmets, face masks, golf shafts, heads, balls and     faceplates, ski and snowboard components including bindings, and     bicycle parts; -   industrial/consumer products and parts including, but not limited     to, face masks, solar panels, turbines and windmills; and -   touch-surfaces which are prone to wear and the spreading of     diseases.

According to exemplary embodiments of the present invention, a method is provided for manufacturing an article having an exposed surface, comprising at least portions that are rendered hydrophobic and/or icephobic and/or biocidal.

Accordingly, in one embodiment, the present invention provides a durable, icephobic, non-isotropic article comprising:

-   at least one metallic material layer having a total thickness of at     least 25 microns comprising at least one metal chosen from the group     consisting of Al, Co, Cu, Fe, Ni, Sn, Ti and Zn; -   a layered and/or graded anisotropic polymeric coating having a total     thickness of at least 10 microns applied to at least part of the     outer surface of the metallic material layer and in intimate, direct     contact therewith comprising:     -   (a) a cured first chemical composition comprising a polymeric         resin at an interface between said polymeric coating and said         metallic material layer extending at least 2.5 microns in height         from the outer surface of the metallic material layer;     -   (b) a cured second chemical composition comprising the polymeric         resin and an icephobic material addition forming an exposed         outer surface of said non-isotropic article extending at least         2.5 microns in depth from the exposed outer surface which, after         curing:         -   (i.b) contains an icephobic material addition composed             entirely of solids representing up to 25% by weight of the             cured second chemical composition,         -   (ii.b) has a Shore D-Scale Hardness of at least 20,         -   (iii.b) has a sand erosion value according to standard ASTM             G76 at an impingement angle of 90 degrees of less than 10             mm³/kg,         -   (iv.b) is hydrophobic, and         -   (v.b) has an ice adhesion of less than 200 kPa as prepared             and of less than 350 kPa after 5 icing/deicing cycles when             measured according to ERDC/CRREL Technical Note 03-4; -   wherein said non-isotropic article exhibits no failure after being     exposed to at least one temperature cycle according to ASTM B553-71     service condition 1, and -   wherein the pull-off strength between the metallic material layer     and an exposed outer surface of the polymeric coating, according to     standard ASTM 4541D, is at least 300 psi.

Accordingly, in another embodiment, the present invention provides a durable, icephobic, non-isotropic article comprising:

-   at least one polymer or polymer composite material layer having a     total thickness of at least 25 microns; -   a layered and/or graded polymeric anisotropic coating having a total     thickness of at least 10 microns applied to at least part of an     outer surface of the polymer or polymer composite material layer and     in intimate, direct contact therewith comprising:     -   (a) a cured first chemical composition comprising a polymeric         resin at an interface between said polymeric coating and said         polymer or polymer composite material layer extending at least         2.5 microns in height from the outer surface of the polymer or         polymer composite material layer     -   (b) a cured second chemical composition comprising the polymeric         resin and an icephobic material addition forming an exposed         outer surface of said non-isotropic article extending at least         2.5 microns in depth from the exposed outer surface which, after         curing:         -   (i.b) contains an icephobic material addition composed             entirely of solids representing up to 25% by weight of the             cured second chemical composition layer,         -   (ii.b) has a Shore D-Scale Hardness of at least 20,         -   (iii.b) has a sand erosion value according to standard ASTM             G76 at an impingement angle of 90 degrees of less than 10             mm³/kg,         -   (iv.b) is hydrophobic, and         -   (v.b) has an ice adhesion of less than 200 kPa as prepared             and of less than 350 kPa after 5 icing/deicing cycles when             measured according to ERDC/CRREL Technical Note 03-4; -   wherein said non-isotropic article exhibits no failure after being     exposed to at least one temperature cycle according to ASTM B553-71     service condition 1, and -   wherein the pull-off strength between the polymer or polymer     composite material layer and an exposed outer surface of the     polymeric coating, according to standard ASTM 4541D, is at least 300     psi.

Accordingly, in another embodiment, the present invention provides a durable, icephobic, and/or biocidal non-isotropic article comprising:

-   a substrate formed of a metallic material or a polymeric material; -   a layered and/or graded polymeric coating having a total thickness     of at least 2.5 microns applied to at least a part of an outer     surface of the substrate and forming an outer surface of the     article, -   wherein the polymeric coating, after curing:     -   (i) contains an icephobic material addition composed entirely of         solids representing up to 25% by weight of the cured polymeric         coating,     -   (ii) contains at least one biocidal powder addition of a         metallic material and/or a metal compound comprising a metal         selected from the group consisting of Ag, CO, Cu, Ni, Sn, and         Zn, said biocidal powder addition representing up to 75% per         weight of the cured polymeric coating,     -   (iii) has a Shore D-Scale Hardness of at least 40,     -   (iv) has a contact angle for water greater than 90 degrees,     -   (v) has an ice adhesion of less than 500 kPa as prepared and         after 5 icing/deicing cycles when measured according to         ERDC/CRREL Technical Note 03-4, -   wherein said non-isotropic article has a pull-off strength between     the substrate and an exposed outer surface of the cured polymeric     coating, according to standard ASTM 4541D, of at least 500 psi, and -   wherein said non-isotropic article after 24 hours at 37° C. displays     a radius of no growth on a zone inhibition test for microorganisms     of at least 0.1 mm.

Accordingly, in another embodiment, the present invention provides a durable, icephobic, and/or biocidal non-isotropic article comprising:

-   at least one metallic material layer having a total thickness of at     least 25 microns comprising at least one metal chosen from the group     consisting of Al, Co, Cu, Fe, Ni, Sn, Ti and Zn; -   a polymeric coating having a total thickness of at least 2.5 microns     applied to at least part of an outer surface of the metallic     material layer which, -   wherein the polymeric coating, after curing:     -   (i) contains an icephobic material addition composed entirely of         solids representing up to 25% by weight of the cured polymeric         coating,     -   (ii) contains at least one biocidal powder addition representing         up to 75% by weight of the cured polymeric coating,     -   (iii) has a Shore D-Scale Hardness of at least 20,     -   (iv) has a sand erosion value according to standard ASTM G76 at         an impingement angle of 90 degrees of less than 10 mm³/kg,     -   (v) is hydrophobic, and     -   (vi) has an ice adhesion of less than 400 kPa as prepared and         after 5 icing/deicing cycles when measured according to         ERDC/CRREL Technical Note 03-4, -   wherein said non-isotropic article exhibits no failure after being     exposed to at least one temperature cycle according to ASTM B553-71     service condition 1, -   wherein said non-isotropic article has a pull-off strength between     the metallic material layer and the exposed outer surface of the     cured polymeric coating, according to standard ASTM 4541D, of at     least 500 psi, and -   wherein said non-isotropic article after 24 hours at 37° C. displays     a radius of no growth on a zone inhibition test for microorganisms     of at least 0.1 mm.

Accordingly, the invention in one exemplary embodiment is directed to an article having on its outer surface a polymeric material coating which is smooth (R_(a)<2.5 microns, preferably <1 microns and more preferably <0.5 microns), hydrophobic and icephobic.

Accordingly, the invention, in another exemplary embodiment is directed to a polymeric coating which adheres well to a metallic or polymeric substrate and, at and near the exposed outer surface, comprises a polymeric material containing one or more silicone additives, e.g., modified silicones.

The following further defines the article of the invention:

Substrate Specification

In one embodiment the base article/substrate the coating is applied to is a metallic material. Typical metals and alloys used comprise at least one element selected from the group consisting of Al, Co, Cr, Cu, Fe, Mg, Ni, Sn, Ti, W, Zn, and Zr, with alloying additions consisting of B, P, C, Mo, S, and W, and particulate additions consisting of carbides, oxides, nitrides and carbon (carbon nanotubes, diamond, graphite, graphite fibers, graphene).

In another embodiment the base article/substrate the coating is applied to can also be a polymeric material comprising at least one of: thermosets such as unfilled or filled epoxy, phenolic or melamine resins, polyester resins, urea resins; thermoplastic polymers such as thermoplastic polyolefins (TPOs) including polyethylene (PE) and polypropylene (PP); polyamides, mineral filled polyamide resin composites; polyphthalamides, polyphtalates, polystyrene, polysulfone, polyimides; neoprenes; polybutadienes; polyisoprenes; butadiene-styrene copolymers; poly-ether-ether-ketone (PEEK); polycarbonates; polyesters; liquid crystal polymers such as partially crystalline aromatic polyesters based on p-hydroxybenzoic acid and related monomers; polycarbonates; acrylonitrile-butadiene-styrene (ABS); chlorinated polymers such polyvinyl chloride (PVC); and fluorinated polymers such as polytetrafluoroethylene (PTFE). Polymers can be crystalline, semi-crystalline or amorphous.

Filler additions can include metals, metal oxides, carbides, carbon (carbon, carbon fibers, carbon nanotubes, diamond, graphite, graphite fibers and graphene), glass, glass fibers, fiberglass, metallized fibers such as metal coated glass fibers, mineral/ceramic fillers such as talc, calcium silicate, silica, calcium carbonate, alumina, titanium dioxide, ferrite, mica and mixed silicates (e.g. bentonite or pumice).

Substrates/base articles are made or shaped by any convenient manufacturing process. It is desirable to suitably prepare a surface of the substrates/base article before it receives a coating. The pretreatment can involve a cleaning step followed by a suitable mechanical or chemical process which increases the surface roughness.

Polymeric Coating Specification

The polymeric coating contains a curable resin which can be any thermoset resin that can be cured or “set” by crosslinking. Particularly suitable are epoxy resins including, but not limited to, solid and liquid epoxies from Bisphenol A, Bisphenol F, Diglycidyl Ether of Bisphenol A (DGEBPA), Diglycidyl Ether of Bisphenol F (DGEBPF), Modified epoxies including Carboxyl terminated Butadiene acrylonitrile polymer (CTBN) adducted epoxies of DGBPA and DGBPF, and Cresyl Glycidyl Ether or n-Butyl Glycidyl Ether or Phenyl Glycidyl Ether modified epoxy resins of DGBPA and DGBPF. Preferred polymeric resins are an epoxy resin with an epoxy-equivalent weight (EEW) between 100 and 1,000, preferably between 200 and 750.

The polymeric coating can also contain an elastomer such as any alkadiene polymer, e.g., neoprene rubber; isoprene rubber; butadiene rubber, and the like. Modified epoxies containing rubber or silicone adducts are also suitable. In addition elastomers can include polyurethanes, ethylene-propylene rubbers (EPR, sometimes called EPM referring to an ASTM standard), ethylene-propylene-diene rubber (EPDM) and silicone based elastomers. Preferred rubbers are carboxyl terminated butadiene acrylonitrile polymers (CTBN) and/or amine terminated butadiene acrylonitrile polymers (ATBN). The polymer coating can be elastomer free (0%), in case elastomers are used its content in any cured layer preferably is kept to no more than 60%, preferably less than 50%, more preferably less than 40%, and less than 30% of the weight of the curable resin or the total weight of the cured layer. When elastomers are present, the elastomer content is preferably at least 5%, more preferably at least 10%, and even more preferably at least 20%. The elastomer does not need to be present throughout the coating in the deposition direction, e.g., an elastomer in the bonding layer in contact with the substrate may be beneficial whereas it is not necessarily required in the outer, icephobic layer, unless it is also the icephobic additive or it is added to, e.g., reduce the Shore D hardness of the outer layer to render it soft and flexible to enhance the shedding of ice.

The polymeric coating typically contains a curing agent. Any curing agent known in the art is suitable for this purpose. Particularly suitable are curing agents selected from the group consisting of amide-type, amine-type and imidazole-type curing agents, more particularly imidazole-type curing agents as well as noble metals. The amount of curing agent is kept to no more than 20%, more preferably less than 10%, and less than 7.5% by weight of the cured layer and/or the weight of the resin, e.g., the epoxy resin content, in the formulation.

The polymeric coating can be fiber reinforced. Examples of reinforcing fibers include glass fibers, aramide fibers, carbon fibers, carbon nanotubes, and the like. Other additives can include fluorinated polymers such as polytetrafluoroethylene (PTFE) or fluorinated silicones as well as pigments to provide a coating with any desirable color. In general, the resin compositions used for forming the polymeric coating can be cured at temperatures below 150° C. For example, curing at about 140° C. for 2 hours, or at 120° C. for 4 hours is generally sufficient to accomplish substantially full curing. Under certain circumstances, however, e.g., for use in repair and overhaul, compositions which cure at room temperature are desirable.

An annealing step can be added to increase the adhesion between the polymeric coating layers and between the polymeric coating and the underlying substrate. The annealing step is a heat treatment step, similar to the curing step, in terms of temperature and duration.

As indicated, the inventive polymeric coating is not homogenous in the deposition direction but layered and/or graded to enable the outer surface to be icephobic due to the presence of an “icephobic additive” whereas the composition of the polymeric coating near the inner surface is optimized for maximizing the bond strength between the organic coating and the underlying substrate.

In addition to thermosets, polymeric coating can also be formulated using thermoplastics such as thermoplastic polyurethanes (TPU).

Icephobic Additive Specification

Icephobic material additions include paraffins, silicones (polysiloxane), preferably epoxy-modified silicones, fluorinated silicones, fluorocarbons, polyurethanes such as polyurethane rubber, fluorinated polyols, polyethers, fluorocarbon elastomers and combinations thereof. The icephobic addition content preferably represents at least 1%, preferably at least 2.5%, more preferably at least 5%, more preferably at least 10%, and even more preferably at least 15% and up to 20% and preferably up to 25% of the weight of the cured layer and/or the weight of the resin, e.g., the epoxy resin content, in the formulation.

Silicones (polysiloxanes) are particularly preferred additives for achieving icephobic behavior. Silicone elastomers are often referred to as silicone-based polymers that have been vulcanized. Albeit technically incorrect, the term “silicone rubber” is often used since it is more descriptive. Silicone elastomers or silicone rubber materials are readily available in a hardness ranging from 10 durometer Shore A (extremely soft) to 60 durometer Shore A (firm, medium soft to medium hard). Properties of silicones are determined by the organic groups attached to the silicon atoms, and can be fluids, resinous materials or rubbery materials. “Silicones” are typically water-repellent and are used as adhesives, lubricants, hydraulic oils and caulks (sealants). For the purpose of increasing icephobicity, silicones with low surface energy and excellent elasticity are desired. As noted above, NuSil™ R-2180 from NuSil Technology, LLC, Santa Barbara, Calif., USA, which is a two-part silicone elastomer dispersed in xylene, is a commonly used commercially icephobic coating.

Particularly suitable icephobic additives include reactive silicones which are multifunctional silicone pre-polymers with reactive terminal end groups such as epoxy-modified silicones.

Biocidal Additive Specification

Preferred biocidal additions include metallic powders or metal compounds, including but not limited to their oxides and halides, comprising at least one element selected from the group consisting of Ag, Co, Cu, Ni, Sn, and Zn. Alloying additions can also include, among other, B, P, C, and S. Particulate additions can include the same or other metals, their chlorides, sulfates, oxides or nitrides as well as various forms of carbon (carbon black, carbon nanotubes, diamond, graphite, graphite dots, graphite fibers, graphene).

Due to the requirement of applying the coating as paint by brushing rolling and/or spraying the preferred average particle size of the biocidal powder additions is in the range of 0.5-100 microns, preferably between 0.5 and 50 microns and more preferably between 0.5 and 25 microns. Paints with biocidal powders with particle sizes in excess of 500 microns tend to settle and are difficult to apply uniformly, biocidal powders with average particle sizes significantly below ˜500 nm can easily disperse in air and constitute health and safety issues. Preferably biocidal additions are self-sterilizing, also referred to as oligodynamic.

Additions further enhancing the biocidal activity of the metal, metal oxide and/or other metal compound powders are contemplated as well. They can include, but are not limited to, carbon (carbon black, graphite, carbon nanotubes and graphene) based additions.

To control the dissolution of biocidal active materials additives which can be electropositive or electronegative to the biocidal active material can be incorporated into the polymeric coating. As an example, in the case of Cu, carbon/graphite can be added to create a galvanic couple accelerating Cu metal dissolution thereby enhancing the biocidal performance. Alternatively, zinc can be used to galvanically protect Cu thereby slowing down the dissolution of Cu and the release of Cu ions and preferentially dissolving also providing some, albeit, lesser biocidal properties than Cu ions of similar concentration. The electropositive or electronegative additive can also be incorporated directly into the biocidally active material, e.g., in the case of Zn and Cu, brass powder can be used which, during use, will be “dezincified”.

There are a number of tests that can be used to evaluate the biocidal properties of materials and coatings. To characterize biocidal behavior of smooth metallic or polymeric surfaces popular tests include the zone inhibition test and the colony forming efficiency test. Using biocidal additive free epoxy or polyurethane based coatings as described herein, metal or metal compound free coatings displayed no biocidal properties, i.e., a zone of inhibition of 0 mm for both Salmonella typhimurium and Listeria monocytogene after exposure of the sample at 37° C. for 24 hrs. The Luria-Bertani media is commonly used tor testing for Salmonella which includes; 10 g/L NaCl, 10 g/l, tryptone, 5 g/L yeast extract, 15 g/L agar dissolved in sterile distilled water; pH 7.0-7.2. The Brain Heart Infusion (BHI) media is commonly used tor testing for Listeria which includes 37 g/L BHI and 15 g/L agar dissolved in sterile distilled water, pH 7.0-7.2. When biocidal additives are added, a distinct zone of inhibition develops depending on a variety of factors, including, but not limited to, the choice of the metallic element and the form it is present in, e.g., in metallic powder form, as metal oxide or as another metal compound. In addition, the average particle size of the biocidal powder addition, the microstructure, e.g., the grain size of the powder and its porosity, if any, also affect the intrinsic biocidal material activity. Lastly, the loading of the biocidal additive in the coating as expressed in either weight or volume percent at or near the outer surface influences the activity and duration of the biocidal properties. The person skilled in the art will know how to adjust the biocidal additive additions to achieve the property requirements specific to the desired application, e.g., with respect to initial biocidal activity and biocidal property duration.

To increase the hardness, wear resistance and enhance the biocidal properties the metallic biocidal powder additions preferably comprise a grain-refined microstructure with an average grain size between 2 and 500 nm, preferably between 5 and 50 nm. Biocidal metal powders can be produced for instance by mechanically grinding nanocrystalline metallic layers produced by electrodeposition as, e.g., disclosed in U.S. Pat. No. 8,691,397, followed by an optional classification into various sieving fractions to narrow the particle size distribution. Other options to produce grain-refined metallic powders directly include electrodeposition, mechanical working, including ball milling and/or high energy milling, mechanical alloying and the like. Fine metal powders are known to oxidize in air and, accordingly, the biocidal active surface may be metallic or covered by metal oxide(s). Alternatively, the biocidal additive may be a metal compound such as a metal halide which will dissolve and release metal cations at much higher rates than metallic materials thereby enhancing the initial biocidal activity at the expense of longevity. Combinations of slowly dissolving metallic powders and quickly dissolving metal compounds can be chosen to enhance the initial biocidal activity while retaining biocidal properties for long durations.

In order to be biocidal the volume fraction of the biocidal agent in at least the exposed surface and to a depth of at least 2.5 microns must be greater than 5%, preferably greater than 20%, more preferably greater than 50% and as high as 95%.

Definitions

The term “substrate” as used herein means a structural product that can be used as a base for an article.

As used herein, the term “metal matrix composite” (MMC) is defined as particulate matter embedded in a metallic matrix.

As used herein, the term “filled” or “reinforced” refers to polymer resins which contain fillers embedded in the polymer, e.g., fibers made of carbon, graphite, carbon nanotubes, graphene, glass and metals; powdered mineral fillers (i.e., average particle size 0.01-25 microns) such as talc, calcium silicate, silica, calcium carbonate, alumina, titanium oxide, ferrite, and mixed silicates. A large variety of filled polymers having a filler content of up to about 75% by weight or volume are commercially available from a variety of sources.

As used herein, “prepreg” is an abbreviation for pre-impregnated reinforcement fabric and/or fiber mats which are commercially available and used to provide structure and reinforcement for composite articles. The prepreg member is either a dry or wet lay-up component. A dry lay-up is typically a pre-formed structure partially formed prior to being placed onto the release layer. A wet lay-up consists of placing a fabric or fibers onto the release layer, whereupon a liquid epoxy composition is subsequently poured onto the fibers to impregnate the fibers. A partial curing step may be applied to the prepreg member where necessary.

As used herein, the term “coating” means a deposit layer applied to part or all of an outer surface of a substrate.

As used herein, the term “coating thickness” or “layer thickness” refers to the depth in the deposition direction and typical thicknesses exceed 25 microns, preferably 100 microns.

The term “bonding layer” as used herein refers to an intermediate layer directly adjacent to the substrate and between the substrate and the outermost coating layer exposed to the elements of the article of manufacture.

As used herein, “exposed surface” and “outer surface” refer to all accessible surface area of an object accessible to the atmosphere and/or a liquid. The “exposed surface area” refers to the summation of all the areas of an article accessible to a liquid.

As used herein, “surface roughness”, “surface texture” and “surface topography” mean a regular and/or an irregular surface topography containing surface structures. These surface irregularities/surface structures combine to form the “surface texture”.

As used herein the term “smooth surface” is characterized by a surface roughness (R_(a)) less than or equal to 1 microns.

The term “epoxy” or “epoxy resin” as used herein refers to a flexible usually thermosetting resin made by copolymerization of an epoxide with another compound having two hydroxyl groups and used predominately in coatings and adhesives.

The term “curable epoxy resin” as used herein refers to resins relying on a ring opening reaction of the epoxy functional group to polymerize/cross-link.

The term “polyurethane” as used herein refers to polymers composed of organic units joined by carbamate (urethane) links. While most polyurethanes are thermosetting polymers that do not melt when heated, thermoplastic polyurethanes are also available. Polyurethane polymers are commonly formed by reacting a di- or tri poly-isocyanate with a polyol. Since polyurethanes contain two types of monomers, which polymerize one after the other, they are classified as alternating copolymers.

The term “epoxy equivalent weight” or “EEW” as used herein is used for formulating epoxy adhesive compositions. EEW is defined as the weight of a resin in grams that contains one equivalent of epoxy.

The term “adhesion promoters” as defined herein contains additives which improve adhesion and strongly adsorb onto the surface of the substrate. Ideally, the adsorption is so strong that rather than being a physical adsorption it has the nature of a chemical bond. Adhesion promoters act at the interface between an organic polymer and an inorganic substrate to enhance adhesion between the two materials.

The term “elastomer” as used herein refers to amorphous polymers maintained above their glass transition temperature, so that considerable molecular reconformation, without breaking of covalent bonds, is feasible. At ambient temperatures, elastomers are thus relatively soft and deformable. Examples of elastomers include polyisoprene (natural and synthetic “rubbers), polyurethanes and silicones (silicone “rubbers”).

The term “rubber” as used herein refers to any polymer comprising an alkadiene (isoprene) as one of its monomers.

The term “silicones”, also known as “polysiloxanes” as used herein refers to polymers that include any synthetic compound made up of repeating units of siloxane or (—Si—O—Si—O—)_(n), which is a chain of alternating silicon atoms and oxygen atoms, combined with carbon, hydrogen, and sometimes other elements.

The term “epoxy modified silicone” as used herein refers to reactive silicones, which can be used to create epoxy-silicone hybrids of high durability. By combining the advantages of epoxies (e.g., good adhesion, high abrasion resistance and good mechanical strength but poor UV stability and low hydrophobicity) and silicones (e.g., good flexibility and elongation, excellent UV stability and hydrophobicity but poor abrasion resistance and adhesion) excellent properties can be obtained.

The term “curing” as used herein refers to cross-linking process that results in a three-dimensional molecular polymeric structure.

The term “curable resin” refers to a resin composition that can be cured by crosslinking.

The term “substantially fully cured” refers to a curable resin that has been subjected to a heat treatment at a temperature that is high enough, and for a time that is long enough, to result in a completion of the crosslinking process.

As used herein the term “curing agent” refers to a substance that is used to harden a material. It is typically applied to polymers to facilitate the cross-linking and bonding of its molecular components.

The term “cross-link” as used herein refers to a bond that links one polymer chain to another. These links may take the form of covalent bonds or ionic bonds and the polymers can be either synthetic polymers or natural polymers.

As used herein, the term “contact angle” or “static contact angle” is referred to as the angle between a static drop of deionized liquid water and a flat and horizontal surface upon which the droplet is placed and, unless otherwise indicated, is determined at room temperature.

As used herein the term “hydrophilic” is characterized by the contact angle for water obtained at room temperature of less than 90°, which means that the liquid water droplet wets the surface.

As used herein the term “hydrophobic” or “wetproof” is characterized by the contact angle for liquid water obtained at room temperature of greater than 90°, which means that the water droplet does not wet the surface.

As used herein, “super-hydrophobic” refers to a contact angle for deionized water at room temperature equal to or greater than 150° and “self-cleaning” refers to a tilt angle of equal to or less than 5°.

As used herein, the term “tilt angle” or “roll-off angle” means the smallest angle between a surface containing a water droplet and the horizontal surface at which the droplet commences to and keeps rolling off at room temperature.

As used herein, the term “icephobic” or “pagophobic” means the ice adhesion strength according to the ice adhesion test described by the U.S. Army Engineer Research and Development Center is less than 500 kPa.

As used herein the term “ice adhesion test” is the one described by the U.S. Army Engineer Research and Development Center, Hanover, N.H., USA, in the ERDC/CRREL Technical Note 03-4 (October 2003).

The term “pull-off strength” as used herein refers to the strength of the adhesive bond between the layered metal construct and the bonding layer (or between the bonding layer and the substrate, whichever is lower). Pull-off strength is measured according to standard ASTM 4541D; its dimension is [force]/[length]. Test results are reported in psi units or, more properly, MPa (1 psi=0.0069 MPa).

As used herein “thermal cycling performance” is characterized by the ANSI/ASTM specification B604-75 section 5.4 Test (Standard Recommended Practice for Thermal Cycling Test for Evaluation of Electroplated Plastics ASTM B553-71). In this test the samples are subjected to a thermal cycle procedure as indicated in Table 1. The sample is held at the high temperature for an hour, cooled to room temperature and held at room temperature for an hour and subsequently cooled to the low temperature limit and maintained there for an hour.

TABLE 1 Thermal Cycle Procedure Information Service Condition High Limit Low Limit 1 (mild) 60° C. −30° C. 2 (moderate) 75° C. −30° C. 3 (severe) 85° C. −30° C. 4 (very severe) 85° C. −40° C.

The term “Shore hardness” as used herein refers to a measure of the resistance a material has to indentation. There are three different Shore Hardness scales (00, A and D) for measuring the hardness of different typically polymeric materials (supersoft gels, soft elastomers and rigid plastics).

As used herein the term “sand erosion” refers to a material loss of an article caused by sand impingement. The ASTM G76 “Standard Test Method for Conducting Erosion Tests by Solid Particle Impingement Using Gas Jets” measures the material loss of a surface caused by gas-entrained solid particle impingement with sand from a jet-nozzle This test method can be used for determining erosion for various particle sizes, velocities, attack angles, environments, etc. The ASTM G76 Conditions used in this specification include an impingement angle as indicated, Al₂O₃ powder abrasive with an average particle size of 50 μm, a gas pressure of 20 psi, a blast duration of 1 min, a particle feed rate of 10.0±2.0 g/min, a distance between the test coupon and nozzle tip of 50±1 mm, compressed nitrogen as the carrier gas, an ambient test temperature, and flat sample panels. The person skilled in the art will know that the erosion rate under otherwise similar conditions depends on the impingement angle. While an impingement angle of 90° is commonly used to characterize various materials, depending on the ductility of the substance being tested, the erosion rate can vastly change with the impingement angle, i.e., ductile materials typically have the lowest erosion rate at 90°, whereas brittle materials experience the lowest erosion values at very low impingement angles as indicated, e.g., in J. Vite-Torres et. al., “Solid Particle Erosion on Different Metallic Materials” Tribology in Engineering, Chapter 5, Intech Open Science, 2013.

As used herein, the term “metal”, “alloy” or “metallic material” means crystalline and/or amorphous structures where atoms are chemically bonded to each other and in which mobile valence electrons are shared among atoms. Metals and alloys are electronic conductors, they are malleable and lustrous materials and typically form positive ions. Metallic materials include Cu, Ag and Co and their alloys and are having a valence of 0.

As used herein, the term “metal compound” refers to a chemical compound that contains one or more metallic elements bonded to another non-metallic element(s). Typically, the metal atom has a positive charge and acts as the cation, typically having a positive valence and not 0 as a metallic material. The metal cation in the compound is bonded to a nonmetallic anion, typically a anion having a negative valence, e.g., a halide. Metal oxides such as CuO or metal salts such as CuCl₂, AgNO₃, CoSO₄ and the like are metal compounds which are not considered a metallic material within the context of this invention.

As used herein “coarse-grained” defines a metallic microstructure having an average grain size greater than 1 micron and up to 500 micron. “At least partially fine-grained” is defined as a metallic microstructure having an average grain size between 2 nm and 1,000 nm. As used herein “amorphous” defines a metallic microstructure lacking crystallinity characterized by a pattern of constituent atoms or molecules which do not repeat periodically in the three dimensions.

As used herein, the term “grain size” refers to a size of a set of constituents or components, e.g., the crystallites, included in a material, such as a nanostructured metallic material. Grains/crystallites are attached to each other and are separated by grain boundaries and grains/crystallites are not equivalent to particles, which are independent “unattached” structures, defined by their particle size.

As used herein, the term “particle-size” refers to the size of a free-flowing powder, or granular material.

As used herein, the terms “biocidal agents”, “biocidal material addition” and “antimicrobial products” refer to agents and/or additives that are destructive to organisms, particularly microorganisms, bacteria and viruses and kill or slow the spread of microorganisms.

As used herein, the term “microorganisms” includes bacteria, viruses, protozoans, and fungi such as mold and mildew.

As used herein, the term “zone inhibition test” refers to assays used to determine the antimicrobial efficacies of the biocidal agents in a semi-solid media. The test protocol for the zone inhibition test includes growing selected bacteria overnight, streaking them onto a semi-solid organic media plate, followed by placing a 1 cm² sample on the bacteria streaks and holding the sample at 37° C. for 24 hrs. Thereafter, the distance the bacteria streak has receded away from the edge of the metal sample is measured and this distance denotes the “radius of no growth”/“zone of inhibition”.

BRIEF DESCRIPTION OF THE DRAWINGS

The features and advantages of the invention will be appreciated upon reference to the following drawings, in which:

FIGS. 1 and 3 are graphs showing the wetting angle, ice adhesion, Shore D hardness as well as the sand erosion properties for impingement angles of 90° and 30° for various polymeric coatings.

FIGS. 2 and 4 are graphs showing the pull-off adhesion strength of selected polymeric coatings applied to various substrates.

FIG. 5 is a perspective view of a reusable, self-sterilizing facemask according to one of the preferred embodiments.

FIG. 6 is an exploded perspective view of FIG. 5.

DETAILED DESCRIPTION OF THE INVENTION

It is well known that the formation, adhesion, and accumulation of ice, snow, frost, glaze, rime, or their mixtures can cause severe problems for solar panels, wind turbines, aircrafts, heat pumps, power lines, telecommunication equipment, as well as land vehicles and marine vessels. These problems generate safety hazards and can result in failure. To address these issues, the fundamentals of interfaces between gases, liquids and solids and solid surfaces at low temperatures need to be taken into account and various approaches to form “icephobic” (pagophobic) surfaces have been proposed. As the person skilled in the art knows different properties may be required to prevent the formation and adhesion of ice, snow, glaze, rime, and frost.

Icephobicity is the ability of a solid surface to repel ice or prevent ice formation due to a certain topographical structure and/or chemical composition of the surface. Icephobic surfaces in this specification are defined by an ice adhesion strength of typically <600 kPa, preferably <500 kPa, preferably <350 kPa, preferably <300 kPa, and more preferably <200 kPa. Slippery, liquid infused porous surfaces (SLIPS) have been proposed for reducing ice adhesion to values as low as 10 kPa, however, after a few iceing-deicing cycles, ice adhesion gradually increases to over 200 kPa. Furthermore, the mechanical durability of SLIPS surfaces is typically poor. Many other approaches have been proposed as well which are capable of reducing the icephobicity, however, achieving and maintaining both icephobcity and long-term durability remains a challenge.

In order to enhance icephobicity, the exposed surface needs to generally exhibit poor adhesion characteristics, however, in most of the commercial applications the icephobic material layer is applied as a homogeneous coating onto a suitable substrate. As a consequence, the “inner surface” of such icephobic coatings, e.g., the surface contacting the underlying substrate, exhibits poor adhesion particularly when containing liquid icephobic additives. Delamination and flaking of the polymeric coating at the interface with the underlying substrate frequently limits its durability even if the coating is formulated to be hard and strong.

In this specification, in one preferred embodiment, therefore the inventors of the present disclosure propose to form anisotropic, icephobic coatings by minimizing adhesion on the exposed outer surface while maximizing adhesion on the inner surface to achieve a good bond at the interface with the underlying substrate. This is achieved by modifying the composition of the icephobic material coating in the deposition direction through layering and/or gradually modulating the chemical composition. In its simplest form the coating contains two layers of different composition.

Similarly, it is well known that selected metallic coatings applied to touch-surfaces can significantly reduce the spread of diseases. The inventive polymeric coatings provide biocidal properties while being highly resistant to abrasive and/or sliding wear, scuffing and scratching. This invention relates to articles coated with polymeric layers containing grain-refined and/or amorphous, biocidal, metallic materials or metallic material compounds, preferably in the form of fine powders, which exhibit anti-microbial, antibacterial, anti-fungal and/or anti-viral behavior for extended periods of time while exhibiting enhanced mechanical durability. It is one aspect of the present invention that the metallic polycrystalline material exhibits bulk ionic dissolution characteristics providing enhanced biocidal efficacy.

One characteristic of a metallic material is related to the stored internal energy of its microstructure. Metallic materials which are sufficiently disordered so that the bulk microstructure is prone to release metal ions in biocidal effective concentrations from the outer surface are desired. This property is intrinsic to a material that possesses a high energy microstructure. As an example, cold working (e.g. rolling) of a fully annealed metal is a common method to increase the concentration of structural defects, in this case dislocations, throughout the microstructure of the metal. The presence of these defects, in turn, increases the stored internal energy of the cold worked metal relative to the same material in the fully annealed, equilibrium state. Another way to increase the internal stored energy of a metal is to refine the size of its constituent crystals or grains. Atoms located at the grain boundary and triple junction (intersection of three grain boundaries) regions are well-known to possess much higher stored energy values compared to those atoms situated within the well-ordered crystal.

When the grain size of the material is decreased, the volume fraction of the material's constituent atoms that are located at intercrystalline sites rises proportionately and, at an average grain size below approximately 300 nm, the stored internal energy contribution of the interfacial atoms becomes discernible. This manifests itself in a tendency for the fine-grained metallic material to exhibit an enhanced ionic dissolution rate relative to its chemically equivalent coarse-grained counterpart. Hence, grain refinement is an effective means to promote the sustained dissolution of metallic material at concentrations that result in enhanced biocidal efficacy. This approach allows the use of powder additions not requiring minimizing the particle size to maximize biocidal efficacy reducing/eliminating the adverse health effects of handling fine powders when preparing and/or applying the coating.

Articles or coatings according to the invention can be formed by incorporating suitable metallic compositions and/or metal compounds in the form of particulates, including, but not limited to, powders, fibers, and shavings, into polymeric coatings which are applied onto permanent or temporary substrates. Suitable permanent substrates include a variety of metal substrates, carbon-based materials selected from the group of graphite, graphite fibers and carbon nanotubes, and polymer substrates, commonly referred to as “plastics”.

In addition to improving biocidal efficacy, grain size reduction/grain refinement is known to increase the hardness, strength, abrasive wear, scuff, and scratch wear resistance of fully-dense metallic materials. Depending on the mechanical properties desired the grain size is suitably reduced to a level required to achieve the desired hardness, strength, abrasive wear, scuff, and/or scratch resistance.

While the addition of metallic materials and/or metal compounds to the polymeric coating typically lowers the contact angle for water and increases the ice adhesion strength, the inventors have surprisingly discovered that sufficient amounts of biocidal powder can be incorporated into the polymeric coating to render the coating biocidal while still maintaining hydrophobic properties and acceptable icephobicity. It also has been surprisingly observed that the ice adhesion strength of polymeric coatings containing metallic material powders frequently decreases with increasing icing/deicing cycles while typically the ice adhesion strength without metallic material additions increases with increasing icing/deicing cycles. In addition it has also been surprisingly discovered that incorporating biocidal powder into the polymeric coating improves adhesion and increases the pull-off strength to all substrates of interest thereby reducing the need for using multilayered coatings.

As highlighted before there are numerous applications and products which greatly benefit from durable coatings which are water and ice repellent, while providing biocidal properties. Applications include reusable face mask housings/shells containing a suitable air filter and sealing the mouth and nose from direct exposure to ambient, unfiltered, air which are worn in all ambient conditions and can be exposed to various form of water from the elements as well as moisture from exhaling, sweat etc. and can become a breeding ground for microorganisms.

FIG. 5 and FIG. 6 depict such a reusable, biocidal face mask 10 for filtering air. The face mask 10 generally comprises an outer shell 12, typically produced from a polymeric material by injection or compression molding, which is reasonably rigid to maintain its shape, provide a protective enclosure and is perforated by holes and/or slits 18 so air can pass in and out relatively unimpeded. The outer shell 12 attaches to a support frame 16, optionally containing a one-way exhale vent 26. A replaceable filter element 14 is secured between the outer shell 12 and the support frame 16. The filter element 14 is designed to capture pollutants and airborne contaminants including, but not limited to carbon monoxide, nitrous oxides, ozone, airborne microorganisms and viruses as well as pollen. The filter element 14 may be conveniently shaped so it does not cover the exhale vent 26 to minimize the air pressure upon exhaling. The support frame 16 supports the filter element 14 and maintains it shape in the face mask 10 while the front shell 12 protects the filter element 14 and inner components of the face mask 10. The face mask 10 includes a head strap 28 attached to the front shell 12 for holding the face mask 10 in place on a user's head. The face mask 10 includes a face seal 24 typically attached to the support frame 16 for providing a flexible and air-tight seal around the nose and mouth of the user. The face seal 24 provides a snug seal to the user's face and prevents air from passing through thereby forcing the air to exclusively be drawn into the face mask 10 through the replaceable filter element 14. The flexible seal 24 can be made of medical grade silicone. To prevent buildup of water condensation and, at subzero centigrade ambient temperatures, possibly ice from plugging the holes/slits 18 in the outer shell 12 and keep the mask free from mold, bacteria and viruses, at least part of the outer shell 12 and the support frame 16 are coated with at least a 2.5 microns thick layer of the durable, water-repellent and icephobic, biocidal coating, according to the present invention. Preferably the outer shell 12 and the support frame 16 are totally encapsulated with the biocidal coating of the present invention.

Epoxies are known for achieving excellent adhesion to a number of substrates including metals due to their polar nature and their ability to create chemical bonds to the surface upon cure. Hard and strong due to high crosslinking, cured epoxies can bear loads and resist wear caused by abrasion over the long term. This good mechanical strength, however, at high crosslink density flexibility decreases and epoxies are known for cracking due to their brittleness and inability to dissipate stresses. Cured epoxies layers require the addition of icephobic material additives to notably reduce ice-adhesion strength and the addition of biocidal materials to destroy undesired microorganisms, bacteria and viruses.

Similarly, polyurethanes are commonly employed as coatings for preventing corrosion of metal articles and to make a variety of materials more durable. Polyurethanes are extremely resilient substances and their mechanical properties can be easily manipulated by optimizing their compositions.

Silicones exhibit high elongation and flexibility that enable the dissipation of stresses and applied energy. Their strong Si—O bond and high surface energy make silicones resistant to atmospheric or chemical attack and less susceptible to degradation from sunlight, water uptake and ultraviolet (UV) light, thereby providing hydrophobic and icephobic properties for extended periods of time.

The inventors of the present disclosure have discovered that combining the adhesion, abrasion resistance and mechanical strength of epoxies with the thermal stability, flexibility and icephobicity of silicones in hybrid systems yields strong and flexible materials with higher resistance to cracking in harsh environments while providing hydrophobic and icephobic properties. Starting out at the metallic or polymeric substrate surface representing the inner coating surface by applying a polymeric coating with a high epoxy content, preferably being substantially free of silicones or having a low silicone content assures a good bond between the polymeric coating and the underlying substrate. Then, as the thickness of the polymeric coating increases, the silicone contents in the deposition direction towards the outer exposed surface can be gradually or stepwise increased. Consequently a polymeric coating is formed ending up with the highest silicone content at the outer, exposed surface, thus providing for an anisotropic polymeric coating which maintains excellent adhesion to the substrate surface while being icephobic on the exposed, outer surface. In one preferred embodiment the same epoxy resin is used throughout the coating, i.e., in both the bonding and the icephobic layer.

Similarly, substituting polyurethanes based coatings for epoxies using otherwise the same approach can yield durable coatings with excellent icephobic properties and high adhesion to the underlying substrates.

This invention relates to articles comprising durable, icephobic coatings. In its broadest aspect the present invention relates to article of manufacture comprising:

-   (i) a substrate comprising a metallic or polymeric material having     an outer surface in direct contact with -   (ii) an anisotropic polymeric coating which     -   (a) on the interface between said polymeric coating and said         substrate contains a substantially fully cured organic resin and         is substantially free of icephobic additives; and     -   (b) on its exposed outer surface contains the same substantially         fully cured organic resin and furthermore contains one or more         solid icephobic additives.

In one preferred embodiment the substrate comprises a metallic material. Examples of suitable metallic materials include metals and alloys of aluminum, cobalt, magnesium, steel, nickel and titanium. The substrate can be an isotropic, layered or graded metallic construct comprising one or more continuous metal layers wherein at least one of the continuous metal layers is a microcrystalline and/or amorphous metal layer or a grain-refined layer having a grain size below 5,000 nm.

In another preferred embodiment the substrate comprises a polymer or polymer composite. Suitable polymers include any known thermoplastic or thermoset. Suitable polymer composites can contain a material selected from the group consisting of carbon, carbon fibers, graphite, graphite fibers, carbon nanotubes and graphene. Other additions such as glass, glass fibers, as well as inorganic and organic fibers or biocidal materials selected from the group of biocidally active metal or compounds are contemplated as well.

The polymeric coating applied to the substrate is anisotropic in the deposition direction, e.g., layered or compositionally graded. The composition of the polymeric coating in contact with the substrate and near the interface with the substrate is chosen to maximize the adhesion strength between the polymeric coating and the substrate. In contrast, the composition of the exposed outer surface of the polymeric coating is chosen to maximize erosion performance and icephobic properties. The transition of the composition of the polymeric coating from the “bonding surface” to the “icephobic surface” and/or “biocidal” surface can be gradual, e.g., by changing the chemical composition from an epoxy or polyurethane rich and silicone and biocidal agent free to an epoxy or polyurethane and silicone and/or biocidal additive containing outer surface providing a graded polymer layer. Alternatively, distinct layers of various compositions can be applied to transition from an epoxy or polyurethane rich, silicone-free and biocidal agent free to an epoxy or polyurethane and silicone and/or biocidal agent containing outer surface. In the case of layering, at a minimum, two distinct polymer layers are applied; however, a multilayer laminate with a total of up to 100 sublayers can be applied. Combination of layered and graded sublayers is also included in the scope of this invention.

In an alternative embodiment the anisotropic polymeric coating is not directly applied to the substrate but formed independently and provided with an adhesive film or an adhesive tape in contact with the bonding layer and the exposed adhesive film is protected by a release liner. Before use, the release liner is removed and the coating is applied to the substrate in a way that the adhesive film forms an intermediate layer between the substrate and the anisotropic polymeric coating. The adhesive film can be epoxy based providing high adhesive strength and preferably cures at or near room temperature. Other options include rubber-, silicone- or acrylic-based adhesive tapes which can also be pressure sensitive adhesives. In one preferred embodiment the adhesive layer replaces the bonding layer and is applied directly onto the icephobic and/or biocidal layer. Such an approach can be used to apply the icephobic and/or biocidal coating conveniently onto any part to render it icephobic and/or biocidal, it is particularly suitable for use in repair and overhaul, e.g., where there is a requirement to patch eroded or deteriorated sections of the coating.

The present invention is based on the discovery that, in the case of applying an icephobic and/or biocidal organic coating to a metallic or polymeric substrate surface, an isotropic coating does not readily achieve the desired overall performance as either adhesion to the underlying substrate or icephobic properties or both are unduly compromised which can have a significant effect on performance and durability. Monolithic coatings optimized for icephobicity and/or biocidal properties were found to have rather poor adhesion to the substrate materials of interest and perform poorly on extended durability tests such as sand or rain erosion frequently resulting in part or the entire coating flaking off the underlying substrate surface resulting in premature failure.

Typically, the polymeric coating according to this invention uses the same ingredients throughout, e.g., the same curable epoxy or polyurethane resin, the same curing agent formulation etc. termed “basic coating formulation”. The main difference in the chemical formulations near the “bonding surface” when compared to near the “icephobic surface” and/or “biocidal surface” is, that, in the case of the “near bonding layer surface” the coating comprises merely the “basic coating formulation” with the optional addition of adhesion promoters, and elastomers. In contrast, “near the outer icephobic and/or biocidal surface” the coating comprises the “basic coating formulation” with the addition of between 1 and 20 weight % of an “icephobic additive” and/or between 5 and 90 weight % of an biocidal additive with the optional addition of other additives, including, but not limited to, abrasive materials to enhance the hardness and erosion resistance of outer and near-outer surface and pigments to achieve any desired color. Consequently, the chemical composition throughout the polymeric coating is similar assuring excellent adhesion of sublayers, if any, to each other and excellent overall cohesive strength of the entire coating. This approach is far superior to, e.g., applying a distinct polymer primer to the substrate followed by the deposition of a distinct and unrelated, icephobic polymeric coating, which can lead to delamination of the “unrelated” polymer layers during use.

Accordingly, the polymeric coating applied to the metallic or polymeric material substrate is anisotropic and comprises, on the surface in contact with the substrate material, a “bonding layer” comprising a curable resin preferably free of silicones and, on the exposed outer surface an “icephobic layer” which, in addition to the same curable resin, contains at least 1 and up to 25 weight percent of a modified silicone. In the case the exposed outer surface is also rendered biocidal a “biocidal layer” which, in addition to the same curable resin, contains at least 5 and up to 95 weight percent of a biocidal additive.

Both, the bonding layer and the outer icephobic and/or biocidal layer have a thickness of at least 5 microns, preferably at least 25 microns and more preferably at least 50 microns.

The bonding layer is deposited directly onto the substrate material and subsequently typically at least partially cured and another cure is performed after the icephobic top coat is applied. Depending on the number of sublayers the total number of curing steps involved is at least 2 but as many as 10+ curing cycles can be used, depending on the number of sublayers applied and the final properties desired.

In another aspect the invention provides a process for coating an article, said process comprising the steps of:

-   providing an article of manufacture having an outer surface, or a     predetermined portion thereof, comprised of a metallic or polymeric     substrate material; -   coating the outer surface of the substrate material, or a     predetermined portion thereof, with a curable polymeric resin of a     first composition; -   substantially partially or fully curing the curable polymeric resin     of the first composition to form a bonding layer; -   coating the outer surface of the bonding layer with a polymeric     resin of a second composition comprising an icephobic additive; -   substantially fully curing the curable polymeric resin of the second     composition to form a durable icephobic exposed outer surface;

In another aspect the invention provides a process for applying a prepreg coating to an article, said process comprising the steps of:

-   providing an article of manufacture having an outer surface, or a     predetermined portion thereof, comprised of a metallic or polymeric     substrate material; -   independently forming and substantially partially or fully curing a     curable polymeric resin of the second composition comprising an     icephobic and/or biocidal additive to form a durable icephobic     and/or biocidal exposed outer surface; -   optionally applying onto the second composition layer a curable     polymeric resin of a first composition and optionally partially or     fully curing the curable polymeric resin of the first composition; -   applying onto the first composition layer, if present, an adhesive     layer and optionally partially or fully curing the multilayer     construct; -   optionally applying onto the adhesive layer a release liner; -   upon use removing the optional release liner from the multilayer     construct and applying it to the metallic or polymeric substrate     material so that the icephobic and/or biocidal layer of the second     composition becomes the exposed outer surface.

As highlighted above, under certain conditions, the use of a bonding layer can be eliminated and an acceptable adhesion can be achieved while still providing water and ice repellent outer surfaces. Such processes results in achieving a very strong bond between the outer exposed coating surface and the underlying core substrate and the processes can be used to manufacture articles in which strong adhesion between the exposed polymeric coating and the underlying substrate is desired or necessary. In addition, the organic coating sublayers are formulated and/or processed to maximize cohesive strength within the polymeric coating sublayers themselves while achieving excellent adhesion between the sublayers as well. The processes are particularly suited for the manufacture of durable articles that require high water repellency, icephobicity, biocidal properties as well as abrasion resistance and flexural, tensile, torsional, impact and/or fatigue strength, such as required for sporting goods, automotive parts, aircraft components, building materials, industrials components exposed to the elements; and the like. It is desirable to pretreat the substrate surface before it receives the polymer coating. The pretreatment can comprise mechanical abrasion and/or etching. Etching can be, e.g., accomplished with permanganate or sulfochromic chemical etch, or with a plasma etch.

The compositions comprising the curable resin can, for example, be applied by spraying. For this purpose the composition desirably uses a solvent in a sufficient amount to obtain the viscosity suitable for spraying. It has been found that preferred solvents have a boiling point of less than 150° C., preferably less than 100° C. The importance of the boiling point of the solvent is related to the need to have the film substantially fully cured. It is important that, after curing, the polymeric coating has substantially no dissolved solvents and does not contain any liquids.

When applied by spraying, both the bonding layer and the icephobic layer are generally applied at about 3 to 20 mg/cm², preferably from 5 to 15 mg/cm². Depending on the thickness desired, it may be advantageous to apply each composition in two or more sprayed layers, with a partial curing (for example 30 minutes at 140° C. or 90° C.) between applications.

After applying the bonding layer and prior to depositing the icephobic outer layer, the bonding layer can be partially or fully cured as well as suitably pretreated. This pretreatment can comprise mechanically roughening and/or etching. Suitable etching processes include chemical etching processes and/or plasma etching.

When applying the icephobic layer, the spraying process described for applying the bonding layer is essentially replicated. Alternative processes can be used as well including, but not limited to, painting, doctor blading and screen printing.

While building up the entire polymeric coating, various curing steps can be performed and repeated, alternatively partial curing steps can be employed or the curing step can be deferred until the entire coating has been deposited.

As the person skilled in the art of organic coatings would appreciate, the organic coating can be applied to the core substrate in an automated production line where, e.g., the substrate to be coated passes from one spray booth to the next with optional partial or total curing and/or surface treatments in between. A multilayer laminate coating can be produced, e.g., changing the composition of the “paint” in each spray station to achieve a “stepwise” transition from the bonding layer composition to the icephobic surface composition. While the organic coating of this invention relies on at least two distinct layers, a multitude of layers, such as 5, or 10 or even more transitional layers can be incorporated between the inner surface (in contact with the substrate) and the outer (exposed) surface of the organic coating. Similarly, rather than having a multilayer laminate with distinct chemical compositions, a gradual change in the composition can be affected in the coating deposition direction and combinations of layered and graded layers are within the scope of this invention as well.

It is also possible to provide the icephobic and/or biocidal polymer layer in freestanding form or supported such as a “pre-preg” as described above. The bonding layer film or pre-preg used in this process can be fabricated from the liquid epoxy formulation using standard industry practices used for fabricating thin film polymeric adhesive films and pre-pregs from solvent bearing formulations. The release liner protecting the adhesive film/transfer tape is removed before use and the anisotropic polymeric coating comprising an icephobic layer, a bonding layer and an additional adhesive layer or, alternatively, the adhesive layer is replacing the bonding layer altogether, is then applied to the substrate. For instance, the icephobic and/or biocidal layer can be applied, e.g., sprayed onto the exposed surface of an adhesive tape which may have a release liner on the opposite side.

Articles or coatings made according to the process of this invention find use in a variety of applications requiring improved durability while retaining enhanced hydrophobic, icephobic and biocidal properties.

EXAMPLES

The following is a description of Working Examples illustrating the benefits of the present disclosure, specifically the formulation of various polymeric coatings and methods of applying and curing the coatings as well as selected properties including the icephobic properties (Working Example I and III) as well as adhesion properties using a variety of substrates (Working Example II and IV). Working Examples V and VI show the benefits of incorporating metal powders into icephobic coating formulations when eliminating the bonding layer.

Example I: Icephobic Epoxy (EP) Coating Formulations, Application and Selected Properties

Various coating formulations were investigated as follows: Nusil™, a commercial product (two-part silicone elastomer dispersed in xylene) available from NuSil™ Technology LLC, Carpinteria, Calif. 93013, USA, which is widely recognized for its icephobic properties as indicated above, was applied to selected substrates by doctor blade whereas the various inventive epoxy-based coatings were applied to the substrates by spraying using a gravity feed type, HVLP (high volume-low pressure) epoxy spray gun operated at 60 psi. In-house paint formulations are provided in Table 2 below. The coated substrates were subsequently cured in a furnace at 140° C. for 2 hours, except for Nusil™, which was cured according to the manufacturer's specifications using four temperatures and durations as follows: RT/30 min, 75° C./45 min, and 150° C./135 min. Total target loading for each sample was 8-12 mg/cm² (thickness: 75-100 microns). If multiple layers were applied, e.g., an icephobic layer on top of the bonding layer, the thickness and loading for each layer was reduced to maintain the overall coating thickness/loading target and a curing step was performed after each layer. After curing, the exposed surface of all samples was smooth and had a surface roughness R_(a)<1 μm.

Cured coating samples produced were characterized as indicated in Table 3. For ease of comparison, the data of the various tests depicted in Table 3 are also shown in FIG. 1, namely the wetting angle, the ice adhesion according to the test described by the U.S. Army Engineer Research and Development Center, Hanover, N.H., USA, in the ERDC/CRREL Technical Note 03-4 (October 2003), the sand erosion value at impingement angles of 90° and 30° according to ASTM G76, and the Shore D hardness.

TABLE 2 In-house Epoxy (EP) Paint Formulations Investigated. Epoxy Resin Icephobic Epoxy Bonding Layer Resin Top Layer Formulation [g] Formulation [g] Epoxy Resin (EEW = 550) 100 100 Elastomer 60 0 Curing Agent 5 5 Adhesion Promoter 8 0 Additives 15 0 Icephobic Additive: 0 7.5 Epoxide Functional Silicone Pre-Polymer Silicone Oil 0 0 Solvent 240 120

The results indicate that all coating surfaces are hydrophobic, that an icephobic additive such as a silicone is required to achieve a low icephobicity value on the first cycle (Nusil™ and silicone top layer containing coatings) and that, after repeated icing/deicing cycles seven times, the ice adhesion of the samples containing the solid silicone remain largely unchanged (modified silicone top layer containing coatings).

The data also reveal that the sand erosion values at 90° impingement with icephobic additions increase compared to the additive free formulation of the bonding layer, however, the erosion values at an impingement angle of 30° experience similar mass losses for all samples. In addition, the Shore D hardness values of the coatings containing epoxy resins are significantly higher than the one for Nusil™.

TABLE 3 Selected Coating Properties Single/Homogenous Layer Two-Layers 6.7% Silicone Elastomer-Free Containing Silicone Free Bonding Layer Epoxy Layer Epoxy Layer plus Outer (Icephobic (Bonding Exposed Surface Nusil ™ Layer) Layer) Icephobic Layer Exposed Surface <1 <1 <1 <1 Roughness, R_(a) [μm] Wetting Angle [°] 119 123 115 123 Cycle 1: 150 110 472 110 Ice Adhesion [kPa] Cycle 7: 305 110 691 110 Ice Adhesion [kPa] Sand Erosion Rate 4.1 4.9 1.9 4.9 @ 90° [mm³/kg] Sand Erosion Rate 2.1 1.8 1.9 1.8 @ 30° [mm³/kg] Shore Hardness 40 (scale A) 70-75 70-75 70-75  0 (scale D) (scale D) (scale D) (scale D)

Example II: Icephobic Epoxy Article Characterization

A number of substrates were selected (4×4 inch panels) for this investigation, namely Al, Ti, stainless steel, carbon fiber reinforced composite and Nylon. The smooth substrates (R_(a)<1 μm) were mechanically abraded with ultra-fine (500 grit) sand paper to a uniform finish, then cleaned and degreased by wiping with a suitable solvent and various coatings described in EXAMPLE I were applied as follows: (i) Nusil™, (ii) an epoxy based, silicone-free, bonding layer, (iii) an epoxy based icephobic layer and (iv) a two layer coating comprising the epoxy based bonding layer on the substrate followed by the epoxy based icephobic outer exposed layer.

TABLE 4 Adhesion Property Evaluation Single/Homogenous Layer 2-Layers 6.7% Silicone Elastomer-Free Containing Silicone Free Bonding Layer Epoxy Layer Epoxy Layer plus Outer (Icephobic (Bonding Exposed Surface Nusil ™ Layer) Layer) Icephobic Layer Pull Off 228 750 1322 1239 Adhesion Strength from Titanium [psi] Pull Off 213 691 1344 1337 Adhesion Strength from Aluminum [psi] Pull Off 201 471 1411 1420 Adhesion Strength from Stainless Steel Grade 304 [psi] Pull Off 210 872 1846 1887 Adhesion Strength from Carbon Fiber Composite [psi] Pull Off 247 428 942 945 Adhesion Strength from Nylon [psi]

The adhesion between the top/exposed surface of any coating and the base substrate was measured by the “pull-off strength” according to standard ASTM 4541D. For ease of comparison, the data of the various samples are depicted in Table 4 are also shown in FIG. 2. The data reveal that layers with the icephobic additive (Nusil™ and icephobic layer) applied directly to the varies substrates have the lowest bond strength, whereas the icephobic additive-free bonding layer and the two-layer structure comprising a bonding layer in direct contact with the substrate and an outer, exposed icephobic layer results in an overall pull-off strength, at times, that exceeded 800 psi as well as 1,000 psi. Articles containing the Nusil™ coating, in all instances, delaminated at the interface of the substrate and the coating. Articles containing a bonding layer in contact with the various substrates, in all instances, showed both signs of delamination as well as cohesive failure, revealing the impressive strength of these samples.

These results indicate that an anisotropic coating (bonding layer+icephobic layer) provides a superior article with excellent durability, bond strength and long lasting icephobic properties.

Example III: Icephobic Polyurethane (PU) Coating Formulations, Application and Selected Properties

A thermoset polyurethane formulation which cures at room temperature with and without the addition of a modified silicone were applied to various substrates by spraying using a gravity feed type, HVLP (high volume-low pressure) spray gun operated at 60 psi and compared to the Nusil™ commercial product described above. In-house paint formulations are provided in Table 5 below. Total target loading for each sample was 8-12 mg/cm² (thickness: 75-100 microns). After curing, the exposed surface of all samples was smooth and had a surface roughness R_(a)<1 μm.

Cured coating samples produced were characterized as indicated in Table 6. For ease of comparison, the data of the various tests depicted in Table 6 are also shown in FIG. 3, namely the wetting angle, the ice adhesion according to the test described by the U.S. Army Engineer Research and Development Center, Hanover, N.H., USA, in the ERDC/CRREL Technical Note 03-4 (October 2003), the sand erosion value at impingement angles of 90° and 30° according to ASTM G76, and the Shore D hardness.

TABLE 5 In-house Polyurethane (PU) Paint Formulations Investigated. Icephobic PU Resin PU Bonding Layer Top Layer Formulation [g] Formulation [g] Thermoset Polyurethane 100 100 Elastomer 0 0 Curing Agent 100 100 Adhesion Promoter 0 0 Additives 0 0 Icephobic Additive: 0 10 Epoxide Functional Silicone Pre-Polymer Silicone Oil 0 0 Solvent 200 200

TABLE 6 Selected Coating Properties Single/Homogenous Layer Two-Layers 4.8% Silicone PU Bonding Containing Silicone Free Layer plus Outer PU Layer PU Layer Exposed Surface (Icephobic (Bonding Icephobic PU Nusil ™ Layer) Layer) Layer Exposed Surface <1 <1 <1 <1 Roughness, R_(a) [μm] Wetting Angle [°] 119 120 120 120 Cycle 1: 150 137 363 137 Ice Adhesion [kPa] Cycle 5: 305 133 532 133 Ice Adhesion [kPa] Sand Erosion Rate 4.1 4.4 4.4 4.4 @ 90° [mm³/kg]*⁾ Sand Erosion Rate 3.5 3.5 3.5 3.5 @ 45° [mm³/kg] Sand Erosion Rate 2.1 2.1 2.1 2.1 @ 30° [mm³/kg] Shore Hardness 40 (scale A) 20 (scale D) 20 (scale D) 20 (scale D)  0 (scale D) *⁾ As reference the sand erosion rate for Al @ 90° is 9.0 mm3/kg.

The results indicate that all coating surfaces are hydrophobic, that an icephobic additive such as a silicone is required to achieve a low icephobicity value on the first cycle (Nusil™ and silicone top layer containing coatings) and that, after repeated icing/deicing cycles five times, the ice adhesion of the samples containing the solid silicone remain largely unchanged (modified silicone top layer containing coatings).

The data also reveal that the sand erosion at all angles of impingement with are similar for all samples. In addition, the Shore D hardness values of the coatings containing PU resins are significantly higher than the one for Nusil™.

Example IV: Icephobic Polyurethane Article Characterization

A number of substrates were selected (4×4 inch panels) for this investigation, namely Al, Ti, stainless steel, carbon fiber reinforced composite and Nylon. The smooth substrates (R_(a)<1 μm) were mechanically abraded with ultra-fine (500 grit) sand paper to a uniform finish, then cleaned and degreased by wiping with a suitable solvent and various coatings described in EXAMPLE III were applied as follows: (i) Nusil™, (ii) a thermoset polyurethane based, silicone-free, bonding layer, (iii) an thermoset polyurethane based icephobic layer and (iv) a two layer coating comprising the thermoset polyurethane based bonding layer on the substrate followed by the thermoset polyurethane based icephobic outer exposed layer.

The adhesion between the top/exposed surface of any coating and the base substrate was measured by the “pull-off strength” according to standard ASTM 4541D. For ease of comparison, the data of the various samples are depicted in Table 7 are also shown in FIG. 4. The data reveal that layers with the icephobic additive (Nusil™ and icephobic layer) applied directly to the varies substrates have the lowest bond strength, whereas the icephobic additive-free bonding layer and the two-layer structure comprising a bonding layer in direct contact with the substrate and an outer, exposed icephobic layer results in an overall pull-off strength that exceeded 1,000 psi. Articles containing the Nusil™ coating, in all instances, delaminated at the interface of the substrate and the coating. Articles containing a bonding layer in contact with the various substrates, in all instances, showed both signs of delamination as well as cohesive failure, revealing the impressive strength of these samples.

These results indicate that an anisotropic coating (bonding layer+icephobic layer) provides a superior article with excellent durability, bond strength and long lasting icephobic properties.

TABLE 7 Adhesion Property Evaluation Single/Homogenous Layer 2-Layers 4.8% Silicone PU Bonding Containing Silicone Free Layer plus Outer PU Layer PU Layer Exposed Surface (Icephobic (Bonding Icephobic PU Nusil ™ Layer) Layer) Layer Pull Off 228 1315 1423 1425 Adhesion Strength from Titanium [psi] Pull Off 213 1298 1455 1420 Adhesion Strength from Aluminum [psi] Pull Off 201 1024 1224 1210 Adhesion Strength from Stainless Steel Grade 304 [psi] Pull Off 210 1677 1685 1650 Adhesion Strength from Carbon Fiber Composite [psi] Pull Off 247 892 1192 1200 Adhesion Strength from Nylon [psi]

Example V: Icephobic and Biocidal Epoxy Property Characterization

In this example, 4×4 inch mild steel panels were used as substrate. The smooth substrates (R_(a)<1 μm) were mechanically abraded with ultra-fine (500 grit) sand paper to a uniform finish, then cleaned and degreased by wiping with a suitable solvent and various single layer coatings as described in Table 2 (EXAMPLE I) “icephobic epoxy resin top layer” were applied with the addition of various amounts of powder additions. The copper powder used had an average particle size of 1 micron and >99% purity. The brass powder (50 Cu/50 Zn) used had an average particle size of 1 micron and >99% purity. Vulcan XC 72R was used as the carbon powder addition. The top layer was applied directly to the steel substrate without the use of a bonding layer.

Cured coated samples were characterized as in the previous examples and are illustrated in Table 8.

TABLE 8 Selected Epoxy Coating Properties. 25% copper + 14% 10% 25% 50% 75% 4% 2% brass, 7% copper copper copper copper carbon in brass carbon in in EP in EP in EP in EP EP in EP EP Exposed Surface <1 <1 <1 1.2 <1 <1 <1 Roughness, R_(a) [μm] Wetting Angle [°]*⁾ 102 93 98 93 94 115 99 Cycle 1: 217 256 394 634 320 79 349 Ice Adhesion [kPa] Cycle 5: 189 259 302 800 129 224 267 Ice Adhesion [kPa] Average of 5 Ice 186 253 336 783 180 182 309 Adhesion Cycles [kPa] Sand Erosion Rate 4.9 4.9 5 5.3 4.9 4.9 4.8 @ 90° [mm³/kg] Pull Off Adhesion 1139 1249 1693 1379 997 1100 808 Strength from Stainless Steel grade 304 [psi] Shore Hardness 75-80 75-80 80-90 80-90 75-80 75-80 75-80 (Scale D) *⁾The contact angle for pure Cu-foil was determined to be 75°

Similar pull-off adhesion results were obtained for metal substrates other than steel or polymeric substrates as illustrated in the previous examples.

Example VI: Icephobic and Biocidal Polyurethane Property Characterization

In this example, 4×4 inch mild steel panels were used as substrate. The smooth substrates (R_(a)<1 μm) were mechanically abraded with ultra-fine (500 grit) sand paper to a uniform finish, then cleaned and degreased by wiping with a suitable solvent and various single layer coatings as described in Table 5 (EXAMPLE III) “icephobic PU resin top layer” were applied with the addition of various amounts of powder additions. The copper powder used had an average particle size of 1 microns and >99% purity. The brass powder (50 Cu/50 Zn) used had an average particle size of 1 microns and >99% purity. Vulcan XC 72R was used as the carbon powder addition. The top layer was applied directly to the steel substrate without the use of a bonding layer.

Cured coating samples were characterized as in the previous examples and are illustrated in Table 9.

TABLE 9 Selected Polyurethane Coating Properties. 10% 25% 50% 75% copper copper copper copper in PU in PU in PU in PU Exposed Surface <1 <1 <1 <1 Roughness, R_(a) [μm] Wetting Angle [°]*⁾ 102 93 98 93 Cycle 1: 286 297 150 266 Ice Adhesion [kPa] Cycle 5: 158 185 191 189 Ice Adhesion [kPa] Average of 5 Ice 224 250 163 253 Adhesion Cycles [kPa] Sand Erosion Rate 4.6 4.7 4.6 4.9 @ 90° [mm³/kg] Pull Off 1103 1260 1549 1712 Adhesion Strength from Stainless Steel grade 304 [psi] Shore Hardness 20 20 20 20 (Scale D) *⁾ The contact angle for pure Cu-foil was determined to be 75°

Similar pull-off adhesion results were obtained for metal substrates other than steel or polymeric substrates as illustrated in earlier examples.

VARIATIONS

The foregoing description of the invention has been presented describing certain operable and preferred embodiments. It is not intended that the invention should be so limited since variations and modifications thereof will be obvious to those skilled in the art, all of which are within the spirit and scope of the invention. 

1. A cured polymeric coating which is compositionally graded or layered to be anisotropic in the deposition direction comprising: (i) a cured first chemical composition extending at least 2.5 microns in height from the outer surface of an underlying substrate; and (ii) a cured second chemical composition having a different chemical composition than the cured first chemical composition, the cured second chemical composition forming an exposed outer surface of the cured polymeric coating and extending at least 2.5 microns in depth from the exposed outer surface, wherein the cured second chemical composition: a) contains a polymeric resin; b) contains at least one icephobic material addition; and c) has an ice adhesion of less than 500 kPa as prepared and after 5 icing/deicing cycles when measured according to ERDC/CRREL Technical Note 03-4.
 2. The cured polymeric coating according to claim 1, wherein the cured second chemical composition contains at least one biocidal powder addition.
 3. The cured polymeric coating according to claim 2, wherein the at least one biocidal powder addition represents at least 5% per volume of the cured polymeric coating.
 4. The cured polymeric coating according to claim 2, wherein the at least one biocidal powder addition is a metallic material and/or a metal compound comprising at least one metal selected from the group consisting of Ag, Co, Cu, Ni, Sn, and Zn.
 5. The cured polymeric coating according to claim 4, wherein the biocidal powder addition has an average particle size of between 0.5 and 25 microns.
 6. The cured polymeric coating according to claim 2, wherein the biocidal powder addition is a metallic powder, and at least part of the metallic powder is grain-refined comprising an average grain size between 2 nm and 500 nm.
 7. The cured polymeric coating according to claim 2, wherein the cured second chemical composition comprises between 1 and 20 weight % of the at least one icephobic material addition and/or between 5 and 90 weight % of the at least one biocidal powder addition.
 8. The cured polymeric coating according to claim 1, wherein the cured second chemical composition contains biocidal agents greater than 5% per volume of the cured second chemical composition.
 9. The cured polymeric coating according to claim 1, wherein the cured second chemical composition contains biocidal agents of up to 95% per volume of the cured second chemical composition.
 10. The cured polymeric coating according to claim 1, wherein the exposed outer surface of the cured polymeric coating after 24 hours at 37° C. displays a radius of no growth on a zone inhibition test for microorganisms of at least 0.1 mm.
 11. The cured polymeric coating according to claim 1, wherein the exposed outer surface of the cured polymeric coating after 24 hours at 37° C. displays a radius of no growth on a zone inhibition test for salmonella or listeria of at least 0.1 mm.
 12. The cured polymeric coating according to claim 1, wherein the cured polymeric coating at room temperature is free of liquids.
 13. The cured polymeric coating according to claim 1, wherein both the first chemical composition and the second chemical composition, prior to curing, comprise one or more curable epoxy resins with an EEW number of between 100 and
 750. 14. The cured polymeric coating according to claim 1, wherein the substrate comprises a metallic material or a polymeric material.
 15. The cured polymeric coating according to claim 1, wherein the cured first chemical composition forms the inner surface contacting the substrate; and said inner surface is rough with a surface roughness of R_(a)>1 micron; and wherein the cured second chemical composition forms the exposed outer surface to atmosphere; and said exposed outer surface is smooth with a surface roughness R_(a)<1 micron.
 16. The cured polymeric coating according to claim 1, wherein the pull-off strength between the substrate and the exposed outer surface of the cured polymeric coating, according to standard ASTM 4541D, is at least 250 psi.
 17. The polymeric coating according to claim 1, wherein the at least one icephobic material addition represents up to 25% by weight of the cured second chemical composition.
 18. The cured polymeric coating according to claim 1, wherein the cured second chemical composition has a contact angle for water at room temperature of greater than 90°.
 19. The cured polymeric coating according to claim 1, wherein the at least one icephobic material addition is composed entirely of solids.
 20. The cured polymeric coating according to claim 1, wherein the at least one icephobic material addition comprises a polysiloxane.
 21. The cured polymeric coating according to claim 20, wherein the polysiloxane comprises an epoxy modified silicone.
 22. The cured polymeric coating according to claim 1, wherein the cured second chemical composition has a Shore D-Scale Hardness of at least
 20. 23. The cured polymeric coating according to claim 1, wherein the cured second chemical composition has a sand erosion value according to standard ASTM G76 at an impingement angle of 90 degrees of less than 10 mm³/kg.
 24. The cured polymeric coating according to claim 1, wherein the cured second chemical composition comprises at least one carbon based additive selected from the group consisting of carbon, carbon fibers, graphite, graphite fibers, carbon nanotubes and graphene.
 25. The cured polymeric coating according to claim 1, wherein the cured first chemical composition includes a polymeric resin arranged at an interface between the cured first chemical composition and the substrate 